      Effect of Cu content on the tribological performance of Cr-N coatings at high temperatures (840°C) 

      Polychronopoulou, K.; Rebholz, Claus; Demas, N. G.; Polycarpou, A. A.; Gibson, P. N. (Affiliation: Department of Mechanical and Manufacturing Eng., University of Cyprus, Nicosia, CyprusAffiliation: Department of Mechanical Science and Eng., University of Illinois at Urbana-Champaign, Urbana, IL, United StatesAffiliation: Institute for Health and Consumer Protection, Joint Res. Centre of the European Commission, Ispra (VA), ItalyCorrespondence Address: Polychronopoulou, K.Department of Mechanical and Manufacturing Eng., University of Cyprus, Nicosia, Cyprus, 2010)
      Cr-N and Cu-Cr-N coatings with Cu content between 3-65 at.%, Cu/Cr ratios in the 0.04-4.5 range and 21-27 at.% N, synthesized by twin e-beam Physical Vapor Deposition (EBPVD) at 450°C, were investigated. Using X-ray ...
    • Article  

      The nanostructure, wear and corrosion performance of arc-evaporated CrBxNy nanocomposite coatings 

      Polychronopoulou, K.; Baker, M. A.; Rebholz, Claus; Neidhardt, J.; O'Sullivan, M.; Reiter, A. E.; Kanakis, K.; Leyland, A.; Matthews, A.; Mitterer, C. (2009)
      The composition, nanostructure, tribological and corrosion behaviour of reactive arc evaporated CrBxNy coatings have been studied and compared to CrN. The CrBxNy coatings were deposited on a commercial Oerlikon Balzers RCS ...
    • Article  

      Synthesis and characterization of Cr-B-N coatings deposited by reactive arc evaporation 

      Polychronopoulou, K.; Neidhardt, J.; Rebholz, Claus; Baker, M. A.; O'Sullivan, M.; Reiter, A. E.; Gunnaes, A. E.; Giannakopoulos, K.; Mitterer, C. (2008)
      Nanocomposite Cr-B-N coatings were deposited from CrB0.2 compound targets by reactive arc evaporation using an Ar/N2 discharge at 500 °C and -20 V substrate bias. Elastic recoil detection (ERDA), x-ray photoelectron ...
    • Conference Object  

      Tribological behavior of CrN and Al-Cr-N coatings 

      Demas, N. G.; Polycarpou, A. A.; Polychronopoulou, K.; Rebholz, Claus (Affiliation: Department of Mechanical Science and Engineering, University of Illinois at Urbana-Champaign, Urbana, IL 61801, United StatesAffiliation: Department of Mechanical and Manufacturing Engineering, University of Cyprus, 1678, Nicosia, CyprusCorrespondence Address: Demas, N. G.Department of Mechanical Science and Engineering, University of Illinois at Urbana-Champaign, Urbana, IL 61801, United States, 2009)
      The tribological behavior of CrN and Al-Cr-N coatings prepared by twin electron-beam evaporation at 450°C was investigated. The composition, structure, mechanical and tribological properties of the coatings were determined ...
    • Article  

      Tribological properties of twin electron-beam evaporated Cr-N and Al-Cr-N coatings under laboratory sliding and drill experiments 

      Polychronopoulou, K.; Demas, N. G.; Rebholz, Claus; Polycarpou, A. A. (2008)
      The tribological behavior of substoichiometric Cr-N and Al-Cr-N coatings prepared by twin electron-beam evaporation at 450°C was studied. Al-Cr-N coatings with Al to Cr ratios in the range of 1-8 (and nitrogen concentrations ...